BUSDE+Z steel plate and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.
BUSDE+Z steel sizes:
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)
BUSDE+Z steel mechanical and process performances:
1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is BUSD, and the corresponding base plate standards is Q/BQB 408-2003.
2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.
Coating Form |
Coating variety
|
Pure zinc coating (single-side)
| |
Equally coating
|
3~90
|
Differential coating
|
3~90, max. coating thickness difference between two sides: 40
|
Single-side coating
|
10~110
|
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm
| |