BR1200HS,BR1200HS steel,BR1200HS steel supplier,BR1200HS steel price,BR1200HS steel plate,HSS-Automotive BR1200HS

HSS-Automotive BR1200HS steel Chemical Composition

Grade	C	Si	Mn	P	B
BR1200HS	0.16~0.20	≤0.40	1.0~1.5	≤0.015	≤0.0035

Remark : Cr,Ti,Nb can be added on a demand

HSS-Automotive BR1200HS steel Mechanical Properties

Grade	Thickness (mm)	Yield strength (MPa)	Tensile strength (MPa)	Elongation A50 (%)
BR1200HS		≥280	≤700	≥18
1200 grade (Heat-treated)		900~1200	≥1200	≥8

Remark : The properties after hot stamping has a close relationship with process. Here only for reference.

Hot stamping is the process by deforming the heated steel in a mould to make parts, which take the advantage of a specific feature of metals that the ductility of metals increases and the yield strength decreases rapidly under a high temperature. The steel sheet is heated to the austenite temperature for hot stamping, and then rapidly cooled in the mould. By such a process, parts with tensile strength above 1400MPa can be manufactured.

HSS-Automotive BR1200HS steel preparation before welding : The mess on the welding area should be cleared to keep it clean and dry .

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As HSS-Automotive BR1200HS Mechanical and HSS-Automotive BR1200HS suppliers, we can supply HSS-Automotive BR1200HS Chemical, HSS-Automotive BR1200HS Mechanical and HSS-Automotive BR1200HS standard for you ,please contact us :