#700L-Z steel,700L-Z steel plate,700L-Z steel supplier,700L-Z steel sheet price,700L-Z steel plate manufacturer

700L-Z steel for automobile beams have high strength and good bending performance, which is suitable for beam parts.

700L-Z steel Chemical composition %

Grade	C	Si	Mn	p	S	Al	Nb	V	Ti	Mo
700L-Z	≤0.10	≤0..50	≤2.10	≤0.025	≤0.010	≥0.015	≤0.09	≤0.20	≤0.15	≤0.50

Remarks : Nb + V + Ti ≤0.22%

700L-Z steel Mechanical Properties

Grade	Yield strength (MPa)	Tensile strength (MPa)	Elongation (%)		180 degree cold bend, diameter
			Thickness＜3mm Lo=80mm, b=20mm	Thickness≥3mm L0=5.65√S0
700L-Z	≥750	800-950	≥10	≥12	2.0a

Remarks :
1 . The yiels strength of 650MPa and 700MPa with thickness ＞8mm can be 20MPa lower .
2 . Samples for the tensile test are taken in rolling direction. Samples for cold bend test are taken transversely .

700L-Z steel size range

Grade	Size (mm)
700L-Z	3.0~12.0 ×900~1600

700L-Z steel plate application :
700L-Z Hot-rolled high strength steel sheets widely used in wheel, beam, carriage, axle, drive shaft, chassis, suspension and other important parts etc.

Shanghai Royal Industry will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As 700L-Z Mechanical and 700L-Z suppliers, we can supply 700L-Z Chemical, 700L-Z Mechanical and 700L-Z standard for you ,please contact us