B35AH250 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.
B35AH250 steel surface is smooth, flat and uniform thickness can be improved fill factor core, adhesion and weldability surface of the insulating film is good, and can improve the corrosion resistance punching
Grade
|
Nominal thickness（mm）
|
tensile strength L（N/mm2）
|
Yield Strength L（N/mm2）
|
Elongation L（%）
|
Hardness HV1
|
Bending frequency (times)
|
Stacking factor（%）
|
B35AH250
|
0.35
|
7.65
|
471
|
337
|
25
|
185
|
≥15
|
Grade
|
Nominal thickness（mm）
|
Theoretical density（kg/dm3）
|
Maximum core loss P17/50
(W/kg)
|
minimum magnetic induction B8
（T）
|
B35AH250
|
0.35
|
7.65
|
2.50
|
1.67
|
HENAN JOIN-WIN IM/EX CORP Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B35AH250 Mechanical and B35AH250 suppliers, we can supply B35AH250 Chemical, B35AH250 Mechanical and B35AH250 standard for you ,please contact us