BR1500HS steel Chemical Composition
|
Grade
|
C
|
Si
|
Mn
|
P
|
B
|
|
BR1500HS
|
0.20~0.25
|
≤0.40
|
1.0~1.5
|
≤0.015
|
≤0.0035
|
Remark : Cr,Ti,Nb can be added on a demand
|
Grade
|
Thickness
(mm)
|
Yield strength
(MPa)
|
Tensile strength
(MPa)
|
Elongation
A50
(%)
|
|
BR1500HS
|
1.75~4.0
|
≥320
|
≤800
|
≥13
|
|
1500 grade (Heat-treated)
|
950~1250
|
150~1800
|
≥6
|
Remark : The properties after hot stamping
has a close relationship with process. Here only for reference.
Hot stamping is the process by deforming
the heated steel in a mould to make parts, which take the advantage of a
specific feature of metals that the ductility of metals increases and the yield
strength decreases rapidly under a high temperature. The steel sheet is heated
to the austenite temperature for hot stamping, and then rapidly cooled in the
mould. By such a process, parts with tensile strength above 1400MPa can be
manufactured.
BR1500HS steel preparation before welding :
The mess on the welding area should be cleared to keep it clean and dry .
HENAN JOIN-WIN IM/EX CORP Will return you
with high-quality products and complete after-sale service with the lowest
price. we committed to exceed customer's expectation on the basis of quality,
price, and delivery. We sincerely hope to establish long-term cooperation
relationship with you on the basis of mutual benefit, reciprocity and common
development. As BR1500HS Mechanical and BR1500HS suppliers, we can supply BR1500HS
Chemical, BR1500HS Mechanical and BR1500HS standard for you ,please contact us ：
Email : pandora@steel-jw.com
Skype : pandora.peng
没有评论:
发表评论