B140H1E+Z electrogalvanized automotive plates
B140H1E+Z electrogalvanized plates and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates, structural parts and reinforcements.
B140H1E+Z electrogalvanized plates and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates, structural parts and reinforcements.
B140H1E+Z electrogalvanized automotive plates sizes:
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)
B140H1E+Z steel plate electrogalvanized automotive plates available coating weight range is given in the following table:
g/㎡
g/㎡
Coating Form |
Coating variety
|
Pure zinc coating (single-side)
| |
Equally coating
|
3~90
|
Differential coating
|
3~90, max. coating thickness difference between two sides: 40
|
Single-side coating
|
10~110
|
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm
| |
B140H1E+Z steel sheet/plate electrogalvanized automotive plates coating bending test:
Steel plates and strips for drawing purpose are subject to coating bending test. No coating strips on the outside surface of a sample( at the spot over 7mm away from two edges of the sample), which is bended by 180 degrees in any direction with bending center diameter of , when its two surfaces are met.
Steel plates and strips for drawing purpose are subject to coating bending test. No coating strips on the outside surface of a sample( at the spot over 7mm away from two edges of the sample), which is bended by 180 degrees in any direction with bending center diameter of , when its two surfaces are met.