B180H2E+Z electrogalvanized plates and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.
B180H2E+Z electrogalvanized automotive plates sizes:
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)
B180H2E+Z steel electrogalvanized automotive plates available coating weight range is given in the following table:
g/㎡
g/㎡
Coating Form |
Coating variety
|
Pure zinc coating (single-side)
| |
Equally coating
|
3~90
|
Differential coating
|
3~90, max. coating thickness difference between two sides: 40
|
Single-side coating
|
10~110
|
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm
| |
Steel plates and strips for cold forming purposes are subject to coating bending test. There are no coating strips on the outside surface of a sample( at the spot over 7mm away from two edges of the sample), which is bended by 180 degrees in any direction. Refer to provisions of relevant base plates for bending center diameter and take 0a as the bending center diameter in case of no requirements by the base plates for it.