SECE,SECE steel,SECE steel plate supplier,SECE steel sheet,SECE steel price,SECE steel plate price

SECE steel plate and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

SECE steel sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

SECE steel mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is SPCC、SPCD、SPCE, and the corresponding base plate standards is Q/BQB 402-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

SECE steel available coating weight range is given in the following table: 
g/㎡

Coating Form	Coating variety
	Pure zinc coating (single-side)
Equally coating	3~90
Differential coating	3~90, max. coating thickness difference between two sides: 40
Single-side coating	10~110
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm

Email : pandora@steel-jw.com

Skyep : pandora.peng

SECD,SECD steel,SECD steel plate,SECD steel sheet price,SECD steel supplier,SECD steel

SECD steel plate and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

SECD steel sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

SECD steel mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is SPCC、SPCD、SPCE, and the corresponding base plate standards is Q/BQB 402-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

Email : pandora@steel-jw.com

Skype : pandora.peng

SECIF,SECIF steel,SECIF steel supplier,SECIF steel plate price,SECIF steel sheet supplier

SECIF steel plate and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

SECIF steel sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

SECIF steel mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is DC05(BSC2), and the corresponding base plate standards is Q/BQB 403-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

Email : pandora@steel-jw.com
Skype : pandora.peng

BUSDE+Z,BUSDE+Z steel,BUSDE+Z steel plate,BUSDE+Z steel supplier,BUSDE+Z steel sheet price

BUSDE+Z steel plate and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

BUSDE+Z steel sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

BUSDE+Z steel mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is BUSD, and the corresponding base plate standards is Q/BQB 408-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

BUSDE+Z steel available coating weight range is given in the following table: 
g/㎡

Coating Form	Coating variety
	Pure zinc coating (single-side)
Equally coating	3~90
Differential coating	3~90, max. coating thickness difference between two sides: 40
Single-side coating	10~110
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm

Email : pandora@steel-jw.com

Skype : pandora.peng

BUFDE+Z steel supplier,BUFDE+Z steel sheet price,BUFDE+Z steel plate supplier,BUFDE+Z steel plate price,BUFDE+Z steel

BUFDE+Z steel plate and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

BUFDE+Z steel sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

BUFDE+Z steel mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is BUFD, and the corresponding base plate standards is Q/BQB 408-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

Email : pandora@steel-jw.com
Skype : pandora.peng

BSUFDE+Z steel supplier,BSUFDE+Z steel plate price,BSUFDE+Z steel sheet price,BSUFDE+Z steel

BSUFDE+Z steel
BSUFDE+Z steel plate and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

BSUFDE+Z steel sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

BSUFDE+Z steel mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is BSUFD, and the corresponding base plate standards is Q/BQB 408-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

BSUFDE+Z steel available coating weight range is given in the following table: 
g/㎡

Coating Form	Coating variety
	Pure zinc coating (single-side)
Equally coating	3~90
Differential coating	3~90, max. coating thickness difference between two sides: 40
Single-side coating	10~110
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm

Email : pandora@steel-jw.com

Skype : pandora.peng

BLDE+Z steel supplier,BLDE+Z steel sheet supplier,BLDE+Z steel plate price,BLDE+Z steel price

BLDE+Z electrogalvanized automotive plates
BLDE+Z electrogalvanized plates and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

BLDE+Z electrogalvanized automotive plates sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

BLDE+Z electrogalvanized automotive plates mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is BLD, and the corresponding base plate standards is Q/BQB 408-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

BLDE+Z electrogalvanized automotive plates available coating weight range is given in the following table:    
g/㎡

Coating Form	Coating variety
	Pure zinc coating (single-side)
Equally coating	3~90
Differential coating	3~90, max. coating thickness difference between two sides: 40
Single-side coating	10~110
Note: 50g/㎡ pure zinc coating weight is equivalent to about 7.1μm

Email : pandora@steel-jw.com
Skype : pandora.peng

BLCE+Z,BLCE+Z steel plate,BLCE+Z steel supplier,BLCE+Z steel sheet price,BLCE+Z steel sheet supplier

BLCE+Z electrogalvanized plates and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

BLCE+Z electrogalvanized automotive plates sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

BLCE+Z electrogalvanized automotive plates mechanical and process performances:

1. The mechanical and process performances of pure zinc coated plates/strips must comply with the stipulations of those of relevant base plates. The base plate grade is BLC, and the corresponding base plate standards is Q/BQB 408-2003.

2. Among the mechanical performances of Zn-Ni alloy coated plates/strips, breakage percent elongation is allowed to be lowered by 2 units against that of relevant base plates, r is allowed to be lowered by 0.2 against that of relevant base plates and other mechanical and process performances shall comply with the stipulations of those of relevant base plates.

Email : pandora@steel-jw.com

Skype : pandora.peng

B410LAE+Z steel plate,B410LAE+Z steel supplier,B410LAE+Z steel sheet price,B410LAE+Z steel plate supplier

B410LAE+Z electrogalvanized plates and strips are featured with good erosion-resistant, high surface quality(O5 plate surface are available) and excellent processing and coating performances. They can be used to manufacture inside an outside automotive plates , structural parts and reinforcements.

B410LAE+Z electrogalvanized automotive plates sizes: 
Nominal thickness: 0.30mm~2.0mm, nominal width: 800mm~1830mm 
(Note: nominal thickness of a plate/strip is sum of base plate thickness and coating thickness.)

B410LAE+Z electrogalvanized automotive plates coating bending test:

1. Steel plates and strips for drawing purpose are subject to coating bending test. No coating strips on the outside surface of a sample( at the spot over 7mm away from two edges of the sample), which is bended by 180 degrees in any direction with bending center diameter of 0a, when its two surfaces are met.

2. Steel plates and strips for cold forming purposes are subject to coating bending test. There are no coating strips on the outside surface of a sample( at the spot over 7mm away from two edges of the sample), which is bended by 180 degrees in any direction. Refer to provisions of relevant base plates for bending center diameter and take 0a as the bending center diameter in case of no requirements by the base plates for it.

Email : pandora@steel-jw.com

Skype : pandora.peng