Sales B50AH1000,B50AH1000 steel,B50AH1000 steel plate,B50AH1000 steel sheet,B50AH1000 steel supplier,B50AH1000 steel plate price

B50AH1000 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B50AH1000 steel surface is smooth, flat and uniform thickness can be improved fill factor core, adhesion and weldability surface of the insulating film is good, and can improve the corrosion resistance punching

B50AH1000 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B50AH1000	0.50	7.85	10.00	1.75

B50AH1000 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B50AH1000	0.50	7.85	360	233	41	114	≥15

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B50AH1000 Mechanical and B50AH1000 suppliers, we can supply B50AH1000 Chemical, B50AH1000 Mechanical and B50AH1000 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B27G120 steel,B27G120 steel plate,B27G120 steel sheet,B27G120 steel sheet supplier,B27G120 steel plate price

B27G120 steel silicon content is about 3% to 5%, and other major iron silicon alloy. Electricity, electronics and military industries indispensable soft magnetic alloy is also the largest output of metal functional materials, mainly used for all kinds of motors, generators and transformers cores.

B27G120 steel properties : Low iron loss, magnetic flux density under a strong magnetic field (magnetic induction) high, smooth surface, uniform thickness and smooth, punching resistance, adhesion and weldability surface of the insulating film is good

B27G120 steel Electromagnetic performance standards

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B27G120	0.27	7.65	1.20	1.80

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B27G120 Mechanical and B27G120 suppliers, we can supply B27G120 Chemical, B27G120 Mechanical and B27G120 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B23G110 steel,B23G110 steel plate,B23G110 steel sheet,B23G110 steel supplier,B23G110 steel price,B23G110 steel sheet supplier

B23G110 steel silicon content is about 3% to 5%, and other major iron silicon alloy. Electricity, electronics and military industries indispensable soft magnetic alloy is also the largest output of metal functional materials, mainly used for all kinds of motors, generators and transformers cores.

B23G110 steel properties : Low iron loss, magnetic flux density under a strong magnetic field (magnetic induction) high, smooth surface, uniform thickness and smooth, punching resistance, adhesion and weldability surface of the insulating film is good

B23G110 steel Electromagnetic performance standards

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B23G110	0.23	7.65	1.10	1.80

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B23G110 Mechanical and B23G110 suppliers, we can supply B23G110 Chemical, B23G110 Mechanical and B23G110 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B23G120 steel,B23G120 steel plate,B23G120 steel sheet,B23G120 steel steel supplier,B23G120 steel sheet price

B23G120 steel silicon content is about 3% to 5%, and other major iron silicon alloy. Electricity, electronics and military industries indispensable soft magnetic alloy is also the largest output of metal functional materials, mainly used for all kinds of motors, generators and transformers cores.

B23G120 steel properties : Low iron loss, magnetic flux density under a strong magnetic field (magnetic induction) high, smooth surface, uniform thickness and smooth, punching resistance, adhesion and weldability surface of the insulating film is good

B23G120 steel Electromagnetic performance standards

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction（T）
B23G120	0.23	7.65	1.20	1.80

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B23G120 Mechanical and B23G120 suppliers, we can supply B23G120 Chemical, B23G120 Mechanical and B23G120 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B27G110 steel,B27G110 steel plate,B27G110 steel sheet,B27G110 steel supplier,B27G110 steel steel plate price

B27G110 steel silicon content is about 3% to 5%, and other major iron silicon alloy. Electricity, electronics and military industries indispensable soft magnetic alloy is also the largest output of metal functional materials, mainly used for all kinds of motors, generators and transformers cores.

B27G110 steel properties : Low iron loss, magnetic flux density under a strong magnetic field (magnetic induction) high, smooth surface, uniform thickness and smooth, punching resistance, adhesion and weldability surface of the insulating film is good

B27G110 steel Electromagnetic performance standards

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction（T）
B27G110	0.27	7.65	1.10	1.80

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B27G110 Mechanical and B27G110 suppliers, we can supply B27G110 Chemical, B27G110 Mechanical and B27G110 standard for you ,please contact us :

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B50AH600,B50AH600 steel,B50AH600 steel plate,B50AH600 steel sheet,B50AH600 steel price,B50AH600 steel supplier

B50AH600 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B50AH600 steel surface is smooth, flat and uniform thickness can be improved fill factor core, adhesion and weldability surface of the insulating film is good, and can improve the corrosion resistance punching

B50AH600 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B50AH600	0.50	7.75	6.00	1.72

B50AH600 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B50AH600	0.50	7.75	418	258	37	145	≥15

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B50AH600 Mechanical and B50AH600 suppliers, we can supply B50AH600 Chemical, B50AH600 Mechanical and B50AH600 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B50AH800,B50AH800 steel,B50AH800 steel plate,B50AH800 steel sheet,B50AH800 steel price,B50AH800 steel supplier

B50AH800 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B50AH800 steel surface is smooth, flat and uniform thickness can be improved fill factor core, adhesion and weldability surface of the insulating film is good, and can improve the corrosion resistance punching

B50AH800 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B50AH800	0.50	7.80	8.00	1.74

B50AH800 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B50AH800	0.50	7.80	366	230	40	119	≥15

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B50AH800 Mechanical and B50AH800 suppliers, we can supply B50AH800 Chemical, B50AH800 Mechanical and B50AH800 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B50AH300,B50AH300 steel,B50AH300 steel plate,B50AH300 steel sheet,B50AH300 steel sheet supplier

B50AH300 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B50AH300 steel surface is smooth, flat and uniform thickness can be improved fill factor core, adhesion and weldability surface of the insulating film is good, and can improve the corrosion resistance punching

B50AH300 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B50AH300	0.50	7.65	3.00	1.67

B50AH300 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B50AH300	0.50	7.65	477	336	29	182	≥15

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B50AH300 Mechanical and B50AH300 suppliers, we can supply B50AH300 Chemical, B50AH300 Mechanical and B50AH300 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B50AH350 steel plate,B50AH350 steel sheet,B50AH350 steel plate supplier,B50AH350 steel sheet supplier,B50AH350 steel price

B50AH350 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B50AH350 steel surface is smooth, flat and uniform thickness can be improved fill factor core, adhesion and weldability surface of the insulating film is good, and can improve the corrosion resistance punching

B50AH350 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B50AH350	0.50	7.70	3.50	1.70

B50AH350 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B50AH350	0.50	7.70	423	270	35	155	≥15

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B50AH350 Mechanical and B50AH350 suppliers, we can supply B50AH350 Chemical, B50AH350 Mechanical and B50AH350 standard for you ,please contact us

Email : pandora@steel-jw.com
Skype : pandora.peng

Sales B50AH470,B50AH470 steel,B50AH470 steel plate,B50AH470 steel sheet,B50AH470 steel plate supplier

B50AH470 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B50AH470 steel surface is smooth, flat and uniform thickness can be improved fill factor core, adhesion and weldability surface of the insulating film is good, and can improve the corrosion resistance punching

B50AH470 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B50AH470	0.50	7.75	4.70	1.72

B50AH470 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B50AH470	0.50	7.75	399	243	36	143	≥15

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B50AH470 Mechanical and B50AH470 suppliers, we can supply B50AH470 Chemical, B50AH470 Mechanical and B50AH470 standard for you ,please contact us :

Email : pandora@steel-jw.com
Skype : pandora.peng

B20AT1500,B20AT1500 steel plate,B20AT1500 steel manufacturer,B20AT1500 steel sheet supplier,B20AT1500 steel price

B20AT1500 mainly low-carbon steel, requires a good cold bending and welding properties, as well as some of the press performance.

B20AT1500 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B20AT1500	0.20	7.65	530	410	18	208	＞5

NOTE:
a. detector according to GB / t228-2002, GB / T 19289-2003
b. above are typical values only for reference does not guarantee
c. L direction refers to the rolling direction

B20AT1500 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B20AT1500	0.20	7.65	15.00	1.61

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B20AT1500 Mechanical and B20AT1500 suppliers, we can supply B20AT1500 Chemical, B20AT1500 Mechanical and B20AT1500 standard for you ,please contact us : info@sg295steel.com

B20AT1200,B20AT1200 steel plate,B20AT1200 steel,B20AT1200 steel manufacturer,B20AT1200 steel sheet supplier

B20AT1200 mainly low-carbon steel, requires a good cold bending and welding properties, as well as some of the press performance.

B20AT1200 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B20AT1200	0.20	7.60	542	435	12	216	＞5

NOTE:
a. detector according to GB / t228-2002, GB / T 19289-2003
b. above are typical values only for reference does not guarantee
c. L direction refers to the rolling direction

B20AT1200 steel Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B20AT1200	0.20	7.60	12.00	1.61

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As B20AT1200 Mechanical and B20AT1200 suppliers, we can supply B20AT1200 Chemical, B20AT1200 Mechanical and B20AT1200 standard for you ,please contact us : info@sg295steel.com