B340LA steel,B340LA steel plate,B340LA steel sheet,B340LA steel sheet supplier,B340LA steel plate supplier

B340LA steel is low carbon steel added with a little alloy elements such as niobium and/or titanium, which will be allowed to form carbide and nitride with carbon and nitrogen and separate these carbide and nitride out of ferritic matrix to increase steel strength. With excellent formability and relatively high strength, it is mainly used for manufacturing structural parts of automobiles such as chairs and cross beams.

B340LA steel product sizes: 
Nominal thickness: 0.45mm~2.0mm, nominal width: 800mm~1850mm

B340LA steel mechanical performances:

Steel grade	Yield strengtha  MPa	Tensile strength Mpa  ≥	After Breakage Percent Elongation (L0=50mm, b=25mm)%≥			180°bending test(b≥20mm)
			Nominal thickness mm
			0.60~<1.0	1.0~<1.6	1.6	Bending center diameter
B340LA	340~460	440	22	24	26	0.5a

1. taking RP0.2 in case of indistinct yield, otherwise ReL。

2. using P14 sample of GB/T228

B340LA steel surface quality:

Grade	Code No.	Features
Relatively high-grade finishing surface	FB(O3)	It is allowed for the existence of a few surface defects which will not affect forming and coating & plating adhesiveness such as minor scratch, impression, pit, roll mark and oxidation tint.
High-grade finishing surface	FC(O4)	One side of relatively good quality is free any remarkable defect visible and the other side must reach FB requirements at leasts.

Email : info@sg295steel.com

Skype : pandora.peng

B410LA steel,B410LA steel plate,B410LA steel sheet,B410LA steel sheet supplier

B410LA steel is low carbon steel added with a little alloy elements such as niobium and/or titanium, which will be allowed to form carbide and nitride with carbon and nitrogen and separate these carbide and nitride out of ferritic matrix to increase steel strength. With excellent formability and relatively high strength, it is mainly used for manufacturing structural parts of automobiles such as chairs and cross beams.

B410LA steel product sizes: 
Nominal thickness: 0.45mm~2.0mm, nominal width: 800mm~1850mm

B410LA steel mechanical performances:

Steel grade	Yield strengtha  MPa	Tensile strength Mpa  ≥	After Breakage Percent Elongation (L0=50mm, b=25mm)%≥			180°bending test(b≥20mm)
			Nominal thickness mm
			0.60~<;1.0	1.0~<;1.6	1.6	Bending center diameter
B410LA	410~560	590	16	17	18	a

1. taking RP0.2 in case of indistinct yield, otherwise ReL。

2. using P14 sample of GB/T228

B410LA steel surface quality:

Grade	Code No.	Features
Relatively high-grade finishing surface	FB(O3)	It is allowed for the existence of a few surface defects which will not affect forming and coating & plating adhesiveness such as minor scratch, impression, pit, roll mark and oxidation tint.
High-grade finishing surface	FC(O4)	One side of relatively good quality is free any remarkable defect visible and the other side must reach FB requirements at leasts.

Email : info@sg295steel.com

Skype : pandora.peng

B140H1 steel,B140H1 steel plate,B140H1 steel sheet supplier,B140H1 steel plate supplier,B140H1 steel sheet

Bake hardening steel (BH steel) refers to steel added with some solid solution carbon atoms by adoption of special chemical compositions and production process. It is a new type of high-efficient automotive steel plates with relative low yield strength at delivery and increased yield strength by certain extents through coating baking after their draw forming. JW STEEL can provide two kind of BH steel, i.e. low carbon BH steel and ultra-low carbon BH steel, and B140H1 steel is featured with good formability and stable bake hardness(BH value). They are widely used for manufacturing cover plates of automobiles such as outside door plates and engine hood plates.

B140H1 steel product sizes: 
Nominal thickness: 0.45mm~2.0mm, nominal width: 800mm~1850mm

B140H1 steel mechanical performances:

Steel Grade	Yield strengtha  MPa	Tensile strength Mpa  ≥	After Breakage Percent Elongation (L0=50mm, b=25mm)%≥	After Breakage Percent Elongation (L0=80mm, b=20mm)%≥	rc  ≥	nc  ≥	Bake hardnessd(BH Value)Mpa  ≥
B140H1	140~230	270	41	-	1.6	0.20	30

1. taking RP0.2 in case of indistinct yield, otherwise ReL。

2. using P14 sample of GB/T228

c. r=(r90+2r45+r0)/4; n= (n90 +2n45+n0)/4. 
d. the user is ss

B140H1 steel tensile strain mark: 
It is guaranteed that no tensile strain mark occurs on B140H1 steel plates and strips at their application within 3 months after they are produced and in case of room temperature storage. However, the user is suggested to use BH steel as soon as possible because they tend to gaining tensile strain marks.

B140H1 steel surface quality:

Grade	Code No.	Features
Relatively high-grade finishing surface	FB(O3)	It is allowed for the existence of a few surface defects which will not affect forming and coating & plating adhesiveness such as minor scratch, impression, pit, roll mark and oxidation tint.
High-grade finishing surface	FC(O4)	One side of relatively good quality is free from any remarkable defect visible and the other side must reach FB requirement s at least.
Ultra high-grade finishing grade	FD(O5)	One side of relatively good quality is free from any defect, namely appearance quality after painting or electrogalvanizing is not affected, and the other side must reach FB requirement at least.

Email : info@sg295steel.com

Skype : pandora.peng

B180H1 steel,B180H1 steel plate,B180H1 steel sheet,B180H1 steel sheet supplier

Bake hardening steel (BH steel) refers to steel added with some solid solution carbon atoms by adoption of special chemical compositions and production process. It is a new type of high-efficient automotive steel plates with relative low yield strength at delivery and increased yield strength by certain extents through coating baking after their draw forming. JW STEEL can provide two kind of BH steel, i.e. low carbon BH steel and ultra-low carbon BH steel, and B180H1 steel is featured with good formability and stable bake hardness(BH value). They are widely used for manufacturing cover plates of automobiles such as outside door plates and engine hood plates.

B180H1 steel product sizes: 
Nominal thickness: 0.45mm~2.0mm, nominal width: 800mm~1850mm

B180H1 steel mechanical performances:

Steel Grade	Yield strengtha  MPa	Tensile strength Mpa  ≥	After Breakage Percent Elongation (L0=50mm, b=25mm)%≥	After Breakage Percent Elongation (L0=80mm, b=20mm)%≥	rc  ≥	nc  ≥	Bake hardnessd(BH Value)Mpa  ≥
B180H1	180~280	340	35	-	1.4	0.18	30

1. taking RP0.2 in case of indistinct yield, otherwise ReL。

2. using P14 sample of GB/T228

c. r=(r90+2r45+r0)/4; n= (n90 +2n45+n0)/4. 
d. the user is ss

B180H1 steel tensile strain mark: 
It is guaranteed that no tensile strain mark occurs on B180H1 steel plates and strips at their application within 3 months after they are produced and in case of room temperature storage. However, the user is suggested to use BH steel as soon as possible because they tend to gaining tensile strain marks.

B180H1 steel surface quality:

Grade	Code No.	Features
Relatively high-grade finishing surface	FB(O3)	It is allowed for the existence of a few surface defects which will not affect forming and coating & plating adhesiveness such as minor scratch, impression, pit, roll mark and oxidation tint.
High-grade finishing surface	FC(O4)	One side of relatively good quality is free from any remarkable defect visible and the other side must reach FB requirement s at least.
Ultra high-grade finishing grade	FD(O5)	One side of relatively good quality is free from any defect, namely appearance quality after painting or electrogalvanizing is not affected, and the other side must reach FB requirement at least.